The influence of Group I metal chlorides on water loss and chloride release from magnesium oxychloride cements

The influence of Group I metal chlorides on water loss and chloride release from magnesium oxychloride cements

Canneson, Elodie, Manier, Suliane and Nicholson, John W. (2011) The influence of Group I metal chlorides on water loss and chloride release from magnesium oxychloride cements. Ceramics-Silikaty, 55 (2). pp. 183-187. ISSN 0862-5468 (Print), 1804-5847 (Online)

Full text not available from this repository.

Abstract

The water loss and chloride release from four different formulations of magnesium oxychloride cement have been studied. The formulations were all based on 25% m/m aqueous MgCl2 and the solutions employed to prepare cements consisted of either MgCl2:water or MgCl2:aqueous MCl (M = Li, Na or K, all MCl salts at 1 mol dm-3). Solutions were mixed with solid MgO at a ratio of 1:1 (m/v) and allowed to harden at room temperature for 1 hour. Five disc-shaped specimens (6 mm diameter × 2 mm thickness) of each were prepared, stored in a desiccating atmosphere and weighed at regular intervals. All were found to lose water rapidly, equilibrating within three hours. Water loss was Fickian to values of Mt/M∞ of around 0.7 in all cases. Diffusion coefficients were slightly smaller than for the additive-free cement (1.52 × 10-6 cm2/s) and fell in the range 1.27-1.39 × 10-6 cm2/s. Equilibrium water losses varied from 23.1% (with NaCl) to 20.0% (with KCl), but only with NaCl did the value differ significantly from that for the additive-free cement (20.7%). Chloride release was increased by the presence of the additives. It followed a consistent pattern, with a maximum generally at about 5 hours, followed by a reduction up to 2 weeks (336 hours). This shows that a proportion of the released chloride was taken back up as the cement matured.

Item Type: Article
Uncontrolled Keywords: magnesium oxychloride, alkali metals, water diffusion, chloride release
Subjects: Q Science > QD Chemistry
Faculty / School / Research Centre / Research Group: Faculty of Engineering & Science
Faculty of Engineering & Science > School of Science (SCI)
Related URLs:
Last Modified: 17 Oct 2016 09:11
URI: http://gala.gre.ac.uk/id/eprint/7205

Actions (login required)

View Item View Item