Skip navigation

Evaluation and control of the adhesiveness of cohesive calcium carbonate particles at high temperatures

Evaluation and control of the adhesiveness of cohesive calcium carbonate particles at high temperatures

Horiguchi, Genki, Kamiya, Hidehiro and García-Triñanes, Pablo ORCID: 0000-0002-4993-2250 (2021) Evaluation and control of the adhesiveness of cohesive calcium carbonate particles at high temperatures. Advanced Powder Technology, 32 (2). pp. 283-289. ISSN 0921-8831 (Print), 1568-5527 (Online) (doi:https://doi.org/10.1016/j.apt.2020.12.009)

WarningThere is a more recent version of this item available.
[img]
Preview
PDF (Publisher VoR)
30721_GARCIA_TRINARES_Evaluation_and_control_of_the_adhesiveness.pdf - Published Version
Available under License Creative Commons Attribution Non-commercial No Derivatives.

Download (1MB) | Preview

Abstract

Understanding the adhesiveness of fine particulate materials at high temperatures is important to achieving the stable, economical operation of various industrial systems. In the present research, two types of calcium carbonate (CaCO3) particles having different mean particle sizes (often used as heat carriers in energy systems) were evaluated. The tensile strengths of beds of these materials were determined at various temperatures by tensile strength measurement tester. The adhesiveness was found to increase greatly at 500 °C even without chemical reactions or sintering, and X-ray diffraction analyses showed thermal expansion of the CaCO3 crystals at 500 °C. Pure alumina (Al2O3) and silica (SiO2) microparticles did not exhibit the same pronounced increases in tensile strength or crystal expansion at this same temperature. Because the surface distances between these primary particles were presumably small, it is proposed that van der Waals forces between the particles greatly increased at high temperatures. The addition of Al2O3 nanoparticles to the CaCO3 decreased the tensile strengths of the powder beds both at ambient temperature and at 500 °C. The experimental data confirm that the surface distances between primary particles were increased upon incorporating the nanoparticles, such that the tensile strength decreased during heat treatment.

Item Type: Article
Uncontrolled Keywords: calcium carbonate; tensile strength; thermal expansion; nanoparticles; van der Waals force
Subjects: Q Science > QD Chemistry
Faculty / School / Research Centre / Research Group: Faculty of Engineering & Science
Faculty of Engineering & Science > School of Engineering (ENG)
Last Modified: 25 Mar 2022 11:27
URI: http://gala.gre.ac.uk/id/eprint/30721

Available Versions of this Item

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

View more statistics