Quantitative evaluation of voids in lead free solder joints

Quantitative evaluation of voids in lead free solder joints

Mallik, Sabuj, Njoku, Jude and Takyi, Gabriel (2015) Quantitative evaluation of voids in lead free solder joints. Applied Mechanics and Materials, 772. pp. 284-289. ISSN 1660-9336

[img] PDF
AMM.772.284-3.pdf - Published Version
Restricted to Repository staff only

Download (449kB)

Abstract

Voiding in solder joints poses a serious reliability concern for electronic products. The aim of this research was to quantify the void formation in lead-free solder joints through X-ray inspections. Experiments were designed to investigate how void formation is affected by solder bump size and shape, differences in reflow time and temperature, and differences in solder paste formulation. Four different lead-free solder paste samples were used to produce solder bumps on a number of test boards, using surface mount reflow soldering process. Using an advanced X-ray inspection system void percentages were measured for three different size and shape solder bumps. Results indicate that the voiding in solder joint is strongly influenced by solder bump size and shape, with voids found to have increased when bump size decreased. A longer soaking period during reflow stage has negatively affected solder voids. Voiding was also accelerated with smaller solder particles in solder paste.

Item Type: Article
Uncontrolled Keywords: Voiding, Soldering, X-ray, Lead Free Solder Paste
Faculty / School / Research Centre / Research Group: Faculty of Engineering & Science > Design, Manufacturing and Innovative Products Research Theme
Last Modified: 01 Aug 2017 09:21
URI: http://gala.gre.ac.uk/id/eprint/13520

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

View more statistics